摘要：通過在不同條件下用磁性可分離Fe/OMC復合材料對水中對氯酚的吸附，研究其吸附性能。以酚醛預聚體(PF)為碳源，三嵌段共聚物F127作為模板劑，硝酸鐵為鐵鹽前驅體，采用溶劑揮發誘導自組裝法一步合成磁性可分離載鐵有序介孔碳材料Fe/OMC。研究了Fe/OMC復合材料用量、溫度及pH等因素對吸附的影響。使用X射線衍射，透射電鏡和N2吸脫附等手段對Fe/OMC復合材料進行表征。得出吸附4-CP的最佳條件為: 吸附時間2 h, 溫度為293K , pH為酸性，在最優吸附條件下, 吸附量達266.mg /g, 對4-CP的去除率超過75%。

關鍵詞：對氯酚、Fe/OMC復合材料、吸附

Abstract：Under different conditions by using magnetic detachable Fe/OMC composite materials on the adsorption of chlorophenol in water to study the adsorption properties.Phenolic prepolymer (PF) as the carbon source, triblock copolymer F127 as a template agent, ferric iron nitrate precursor, solvent evaporation induced self-assembly step synthesis of magnetic iron contained separable ordered mesoporous carbon materials Fe/OMC. Of the Fe/OMC composite materials consumption, temperature and PH on the adsorption effect. Using X-ray diffraction, transmission electron microscopy, N2 adsorption-desorption by means of Fe/OMC composite materials were characterized. Adsorption of 4-CP obtained the best conditions were: adsorption time of 2 h, temperature of 293K, PH is acidic, the optimal adsorption conditions, the adsorption capacity 266.mg/g, the removal of more than 4-CP 75%.

Keywords: 4-CP, Fe / OMC composite materials, adsorption

　　　本文以酚醛預聚體(PF)為碳源，三嵌段共聚物F127作為模板劑，硝酸鐵為鐵鹽前驅體，采用溶劑揮發誘導自組裝法一步合成磁性可分離載鐵有序介孔碳材料Fe/OMC，并研究了Fe/OMC復合材料用量、溫度及pH等因素對對氯酚溶液吸附的影響。使用X射線衍射，透射電鏡和N2吸脫附等手段對Fe/OMC復合材料進行表征和分析。

（1）Fe/OMC復合材料具有較窄的孔徑分布。其孔徑大小為4.07nm，BET比表面積644m2/g，孔容為0.33cm3/g。

（2）評價磁性可分離載鐵有序介孔碳材料Fe/OMC對對氯酚的吸附性能，利用XRD,，TEM,，N2吸脫附研究方法對磁性可分離載鐵有序介孔碳材料Fe/OMC進行表征，研究包括材料投加量、溫度等因素對復合材料針對于對氯酚的吸附性能的影響，同時計算相應吸附容量。實驗得出吸附4-CP的最佳條件為: 吸附時間2 h, 溫度為293K ,PH為酸性，在最優吸附條件下, 吸附量達266.mg /g, 對4-CP的去除率超過75%。

（3）準二級動力學模型能夠較好的描述Fe/OMC復合材料對水溶液中4-CP的吸附動力學過程(具有較高的R值)。

（4）Langmuir吸附模型能更好地描述Fe/OMC復合材料對4-CP的吸附行為。